Kalrez® perfluoroelastomer parts provide best in class chemical resistance for exploration and production services while also meeting the industry standard requirements.
| Excellent resistance to fluorine gas |
|
| Very low outgassing properties |
|
| Very low moisture content |
|
| Excellent (low) compression set properties |
|
| Outstanding thermal stability |
|
| Fabs Choose Kalrez® 8900 for Improved Performance |
|
| Excellent retention of physical properties at elevated temperatures |
|
| Gross Weight | Net Weight | Carton Each | Carton Length | Carton Weight | Carton Height |
|---|---|---|---|---|---|
| 0 | 0 | 0 | |||
| 0 | 0 | 0 | |||
| 0 | 0 | 0 |
| Property | Value | Unit | Method |
|---|---|---|---|
| Hardness | ASTM D2240 and D1414 (AS568 K214 O-ring test specimens) | Shore M (O-ring) | 85 |
| ASTM D2240 (Plied slab test specimens) | Shore A (plied slab) | 76 | |
| Compression Set, 70 hr. at 204 °C (400°F) | ASTM D395B and D1414 (AS568 K214 O-ring test specimens) | % | 8 |
| Compression Set, 70 hr. at 300 °C (572°F) | ASTM D395B and D1414 (AS568 K214 O-ring test specimens) | % | 32 |
| Tensile Strength at Break | ASTM D412 and D1414 (AS568 K214 O-ring test specimens) | MPa (psi) | 20.94 (3037) |
| Color | - | — | Black |
| Max. Application Temperature | Qnity proprietary test method | °C (°F) | 325 (617°F) |
| Elongation at Break | ASTM D412 and D1414 (AS568 K214 O-ring test specimens) | % | 135 |
| 100% Modulus | ASTM D412 and D1414 (AS568 K214 O-ring test specimens) | MPa (psi) | 13.33 (1933) |
| Compression Set, 70 hr. at 325 °C (617°F) | ASTM D395B and D1414 (AS568 K214 O-ring test specimens) | % | 59 |
|
Fabric/material |
SBO 8900 |
|---|---|
|
Design |
8900 |
|
Seam |
8900 |
|
Packaging |
8900 |
|
Hazard |
|
|
Coated Material |
SBO 8900 |
|
Features |
SMALL BLACK ORING |
|
Color |
BLACK |