Kalrez® perfluoroelastomer parts provide best in class chemical resistance for exploration and production services while also meeting the industry standard requirements.
| Low erosion rate and ultra-low particle generation in oxygen and fluorine-based plasmas |
|
| Very low outgassing properties and metals content |
|
| Excellent resistance to dry process chemistry |
|
| Particle Generation |
|
| Excellent elastic recovery and low compression set properties |
|
| Plasma Resistance |
|
| Excellent thermal stability |
|
| Gross Weight | Net Weight | Carton Each | Carton Length | Carton Weight | Carton Height |
|---|---|---|---|---|---|
| 0 | 0 | 0 | |||
| 0 | 0 | 0 | |||
| 0 | 0 | 0 |
| Property | Value | Unit | Method |
|---|---|---|---|
| Hardness | ASTM D2240 (Plied slab test specimens) | Shore A (plied slab) | 70 |
| ASTM D2240 & D1414 (AS568 K214 O-ring test specimens) | Shore M (O-ring) | 74 78 | |
| Elongation at Break | ASTM D412 (Dumbbell test specimens) | % | 238 |
| Max. Application, Temperature | Qnity proprietary test method | °C (°F) | 300 (572) |
| 100% Modulus | ASTM D412 (Dumbbell test specimens) | MPa (psi) | 5.17 (750) |
| Tensile Strength at Break | ASTM D412 (Dumbbell test specimens) | MPa (psi) | 15.67 (2273) |
| Compression Set, 70 hr. at 250°C (482°F) | ASTM D395B & D1414 (AS568 K214 O-ring test specimens) | % | 21 |
| Color | - | — | Amber Translucent |
| Compression Set, 70 hr. at 300°C (572°F) | ASTM D395B & D1414 (AS568 K214 O-ring test specimens) | % | 53 |
| Compression Set, 70 hr. at 204°C (400°F) | ASTM D395B & D1414 (AS568 K214 O-ring test specimens) | % | 17 18 |
|
Fabric/material |
LWO 9100 |
|---|---|
|
Design |
9100 |
|
Seam |
9100 |
|
Packaging |
9100 |
|
Hazard |
|
|
Coated Material |
LWO 9100 |
|
Features |
LARGE WHITE ORING |
|
Color |
WHITE |